The Effect of Postmastectomy Radiation Therapy on Breast Implants: Material Analysis on Silicone and Polyurethane Prosthesis.

INTRODUCTION: The pathogenic mechanism underlying capsular contracture is still unknown. It is certainly a multifactorial process, resulting from human body reaction, biofilm activation, bacteremic seeding, or silicone exposure. The scope of the present article is to investigate the effect of hypofractionated radiotherapy protocol (2.66 Gy × 16 sessions) both on silicone and polyurethane breast implants. METHODS: Silicone implants and polyurethane underwent irradiation according to a hypofractionated radiotherapy protocol for the treatment of breast cancer. After irradiation implant shells underwent mechanical, chemical, and microstructural evaluation by means of tensile testing, infrared spectra in attenuated total reflectance mode, nuclear magnetic resonance, and field emission scanning electron microscopy. RESULTS: At superficial analysis, irradiated silicone samples show several visible secondary and tertiary blebs. Polyurethane implants showed an open cell structure, which closely resembles a sponge. Morphological observation of struts from treated polyurethane sample shows a more compact structure, with significantly shorter and thicker struts compared with untreated sample. The infrared spectra in attenuated total reflectance mode spectra of irradiated and control samples were compared either for silicon and polyurethane samples. In the case of silicone-based membranes, treated and control specimens showed similar bands, with little differences in the treated one. Nuclear magnetic resonance spectra on the fraction soluble in CDCl3 support these observations. Tensile tests on silicone samples showed a softer behavior of the treated ones. Tensile tests on Polyurethane samples showed no significant differences. CONCLUSIONS: Polyurethane implants seem to be more resistant to radiotherapy damage, whereas silicone prosthesis showed more structural, mechanical, and chemical modifications.

The impact of Smad3 loss of function on TGF-ß signaling and radiation-induced capsular contracture.

BACKGROUND: Capsular contracture remains a major problem following prosthetic breast implantation, especially in patients undergoing irradiation. Recent studies suggest that such radiation injuries are a cascading process of cytokine activation, with transforming growth factor (TGF)-ß acting as the "master switch." Because TGF-ß signals through phosphorylation of Smad3, a plausible approach to abate TGF-ß-induced capsular contracture would be to interrupt Smad3 signaling. To test this hypothesis, capsular contracture formation in wild-type and Smad3 knockout mice was compared using micro-computed tomographic and histologic examination. METHODS: On day 0, 48 mice were implanted with bilateral silicone gel implants. Postoperatively, animals were imaged using live-scan micro-computed tomographic scanning. Animals in the radiation arm then received a 10-Gy directed radiation dose. On postoperative days 21, 28, 35, and 42, animals were imaged again. Histologic evaluation was performed at necropsy. RESULTS: Irradiated implants in the wild-type mice demonstrated shape and contour deformation on micro-computed tomographic scanning beginning on postoperative day 21 and progressing through day 42. Conversely, micro-computed tomographic scanning of irradiated implants in knockout mice demonstrated few changes from day 0 through day 42. Corresponding histologic specimens from wild-type mice demonstrated irregular capsules composed of disorganized collagen that became thicker from day 21 to day 42. Irradiated knockout specimen maintained thin capsules from day 21 through day 42. CONCLUSIONS: In this work, inhibiting TGF-ß signaling led to a reduction in radiation-induced capsular contracture as measured by micro-computed tomographic and histologic evaluation. The results of this study suggest a promising target for the prevention of capsular contracture through the development of anti-Smad3/TGF-ß-based therapies.